性能项目试验条件[状态]测试方法测试数据数据单位物理性能比重--3ASTMD7921.04g/cm³23°CISO11831.04g/cm³熔流率(熔体流动速率)(200°C/5.0kg)
ASTMD12383.5g/10min溶化体积流率(MVR)(220°C/10.0kg)
ISO113333.0cm³/10min收缩率
ISO294-40.40到0.70%硬度洛氏硬度(R级)
ASTMD785112
机械性能抗张强度屈服4ASTMD63843.6MPa屈服ISO527-2/5042.0MPa断裂ISO527-2/5031.0MPa伸长率断裂4ASTMD63825%断裂ISO527-2/5025%弯曲模量--5ASTMD7902340MPa--6ISO1781900MPa弯曲强度--5ASTMD79068.4MPa--6ISO17865.0MPa冲击性能简支梁缺口冲击强度-30°CISO17912kJ/m²23°CISO17926kJ/m²悬壁梁缺口冲击强度23°C,3.20mmASTMD256240J/m23°C,6.40mmASTMD256210J/m-30°CISO180/1A11kJ/m²23°CISO180/1A25kJ/m²热性能载荷下热变形温度1.8MPa,未退火ASTMD64885.0°C1.8MPa,未退火ISO75-2/A83.0°C1.8MPa,退火ASTMD64895.0°C1.8MPa,退火ISO75-2/A97.0°C维卡软化温度--ASTMD15257105°C--ISO306/A50104°C--ISO306/B5096.0°C线形热膨胀系数-流动
ISO11359-29.1E-5cm/cm/°C可燃性UL阻燃等级(1.5mm)
UL94HB